ABS/PA GF 8

Composite based on ABS/PA GF 8 (a mixture of acrylonitrile butadiene styrene and polyamide PA6) with the addition of 8% fiberglass.
Suitable for printing end products where high impact resistance and UV resistance are required.
It is inert to most of the available chemical solvents (ideal for printing under-hood parts and auto-tuning).

For best results, it is recommended to dry before printing for 2-3 hours at a temperature of 65-75°C.

ATTENTION! Plastic is abrasive, it is recommended to print using a steel nozzle

Print Options:

• Nozzle temperature 260-300°C
• Printing table temperature 110-120°
• Blowing the model is not recommended
• Print speed up to 80 mm / s
• Plastic feed (Flow) 97-100%
• Nozzle diameter from 0.4 mm (min)
• Min. layer height from 0.1 mm
• Volume resistance 1E13-1E11 Ohm * m
• Softening temperature according to VICK 118°C
• Rod diameter tolerance 0.03 mm
• Quantity per coil ~ 285m
• Maximum tensile strength 55 Mpa
• Shore D Hardness –
• Elongation at break 6-12%
• Tensile modulus of elasticity 3100 Mpa
• Heat resistance (min / max) -50 to +120°C
• Density 1.12 g / cm3
• Notched Sharpie impact strength (+23°C) 25 kj / m2
• Notched Sharpie impact strength (-30°C) 6 kj / m2
• Shrinkage in the manufacture of products 0.3-0.5%